Publication Date:
2006-02-14
Description:
Deep level transient spectroscopy reveals that the main electron traps for one-MeV electron irradiated GaAs cells are E9c)-0.31, E(c)-0.90 eV, and the main hole trap is due to the level. Electron trap density was found to vary from 3/tens-trillion ccm for 2/one quadrillion cm 3/3.7 quadrillion cm for 21 sextillion cm electron fluence for electron fluence; a similar result was also obtained for the hole trap density. As for the grown-in defects in the Al(x)Ga(1-x)As p-n junciton cells, only two electron traps with energies of E(c)-0.20 and E(c)-0.34 eV were observed in samples with x = 0.17, and none was found for x 0.05. Auger analysis on the Al(x)Ga(1-x) As window layer of the GaAs solar cell showed a large amount of oxygen and carbon contaminants near the surface of the AlGaAs epilayer. Thermal annealing experiment performed at 250 C for up to 100 min. showed a reduction in the density of both electron traps.
Keywords:
ENERGY PRODUCTION AND CONVERSION
Type:
NASA. Lewis Research Center Space Photovoltaic Res. and Technol. 1983; p 91-101
Format:
text