Publication Date:
2019-01-25
Description:
In SPRAT XI, we proposed that p(sup +)n diffused junction InP solar cells should exhibit a higher conversion efficiency than their n(sup +)p counterparts. This was mainly due to the fact that our p(sup +)n (Cd,S) cell structures consistently showed higher V (sub OC) values than our n(sup +)p (S,Cd) structures. The highest V(sub OC) obtained with the p(sup +)n (Cd,S) cell configuration was 860 mV, as compared to the highest V(sub OC) 840 mV obtained with the n(sup +)p (S,Cd) configuration (AMO, 25 C). In this work, we present the performance results of our most recent thermally diffused cells using the p(sup +)n (Cd,S) structure. We have been able to fabricate cells with V(sub OC) values approaching 880 mV. Our best cell with an unoptimized front contact grid design (GS greater than or equal to 10%) showed a conversion efficiency of 13.4% (AMO, 25 C) without an AR coating layer. The emitter surface was passivated by a -50A P rich oxide. Achievement of such high V(sub OC) values was primarily due to the fabrication of emitter surfaces, having EPD densities as low as 2E2 cm(sup -2) and N(sub a)N(sub d) of about 3E18 cm (sup -3). In addition, our preliminary investigation of p(sup +)n structures seem to suggest that Cd-doped emitter cells are more radiation resistant than Zn-doped emitter cells against both high energy electron and proton irradiation.
Keywords:
ENERGY PRODUCTION AND CONVERSION
Type:
Twelfth Space Photovoltaic Research and Technology Conference (SPRAT 12); p 7
Format:
text
Permalink