Description / Table of Contents:
Investigations into stress corrosion of high strength rope wires in condensating waterIn stress corrosion tests uncoated, galvanized and aluminized rope wires were submitted to the influence of periodically condensating water. Real concentrations of atmospheric contaminants as chlorides, carbon dioxide and sulfur dioxide were added, too.Fractures only were caused under conditions of crevice corrosion as in covered zones. The added contaminants and contact elements, too, did not especially influence fractures. Under the fixed test conditions the life time of the galvanized wires was reduced in relation to the uncoated and aluminized wires.
Notes:
Es wurde der Einfluß einer häufigen Schwitzwasserbeaufschlagung auf das Rißkorrosionsverhalten schwarzer, verzinkter und aluminierter Drähte für Seile untersucht. Den Korrosionszellen wurden auch Schadstoffe, u.a. Chloride, Kohlendioxid und Schwefeldioxid in praxisnahen Konzentrationen zugegeben. Brüche erfolgen nur im Bereich von Kontaktteilen, wo Spaltkorrosionseffekte wirksam werden. Für das Auftreten von Brüchen ist die Art der zusätzlichen Verunreinigungen und die Art von Kontaktelementen nicht von entscheidender Bedeutung. Unter den hier gewählten Versuchsbedingungen ist das Zeitstandverhalten der feuerverzinkten Drähte ungünstiger als jenes von schwarzen bzw. aluminierten Drähten.
Additional Material:
18 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19810320503