ISSN:
0887-6266
Schlagwort(e):
ionic conductivity
;
DC conductivity
;
rigid-rod polymer
;
depletion measurement
;
X-ray scattering
;
anisotropic
;
polymer electrolyte
;
polyelectrolyte
;
conducting polymers
;
Physics
;
Polymer and Materials Science
Quelle:
Wiley InterScience Backfile Collection 1832-2000
Thema:
Chemie und Pharmazie
,
Physik
Notizen:
The conductivity study results of lithium-doped sulfonated PBI, a conjugated rigid rod polymer, poly[(1,7-dihydrobenzo[1,2-d:4,5-d′]dimidazole-2,6-diyl)-2-(2-sulfo)-p-phenylene], derivatized with pendants of propane sulfonate Li+ ionomer are reported. The room-temperature DC four-probe conductivity parallel to the surface of cast films was as large as 8.3 × 10-3 S/cm. Similar measurements with an eight-probe configuration showed no difference between bulk and surface conductivity. The ionic nature of the conductivity was indicated by constant voltage depletion experiments and by secondary ion mass spectroscopy measurements of the residues near the electrodes. The DC two-probe conductivity measured transverse to the sample surface was three to four orders of magnitude smaller than longitudinal conductivity, while the AC two-probe conductivity was even less. Electron microscopy indicated that the films had a layered structure parallel to the surfaces. This structural anisotropy was confirmed by refractive index values obtained from wave-guide experiments and by wide angle X-ray scattering. © 1997 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 35: 2925-2933, 1997
Zusätzliches Material:
11 Ill.
Materialart:
Digitale Medien
Permalink