ISSN:
1573-4889
Keywords:
acoustic emission
;
oxide failure
;
mechanisms
;
iron oxide
;
nickel oxide
Source:
Springer Online Journal Archives 1860-2000
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Notes:
Abstract A small four-point-bend jig has been used in a scanning electron microscope (SEM) to monitor the tensile fracture processes in iron and nickel oxide scales in situ. The scales were 3–40 μm thick, the strain rate was 4×10−5 sec−1 and acoustic emission (AE) was used to correlate signals with specific cracking events. The technique provided detailed information of the failure processes, and several micrographs were taken as the crack pattern developed during testing. Failure started with short random through-scale cracks. These cracks soon formed a regular pattern. Spallation only occurred at much higher strains and resulted in very energetic AE signals. These signals were used together with the SEM observations to determine the strain to cause spallation. Measurements of the crack spacing as a function of strain showed that plastic stress relaxation by interfacial slip and/or substrate yielding processes affected cracking. Thus, the oxide remained attached to the substrate longer than would be expected from purely elastic behavior. An analysis based on the observed crack spacing at the onset of spallation gave ratios of 0.8–1.9 and ∼0.9 between tensile and interfacial strength for iron and nickel oxides scales, respectively.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF01046759
Permalink