ISSN:
1662-9752
Source:
Scientific.Net: Materials Science & Technology / Trans Tech Publications Archiv 1984-2008
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Notes:
The creep resistance of one kind of Zirconium based alloy with Niobium, Iron,Chromium , Tin alloying elements was investigated, the creep curve ( e-t) was obtained in stress levels of 117MPa 、137MPa、157MPa respectively by holding 200 hours at 400°C. The results show that the creep resistance of this alloy is much better than that of Zircaloy-4. The microstructure of post- creep test was observed by TEM, which shows that the dislocation morphology is changed from dislocation lines to dislocation cells with strain increasing , and some precipitates grow larger. It is concluded that the creep is controlled by dislocation climb-glide diffusion mechanism
Type of Medium:
Electronic Resource
URL:
http://www.tib-hannover.de/fulltexts/2011/0528/02/09/transtech_doi~10.4028%252Fwww.scientific.net%252FMSF.475-479.1405.pdf
Permalink