Publication Date:
2011-09-15
Description:
For a control rod element of the Very High Temperature Reactor, a carbon fiber reinforced carbon matrix composite (C/C composite) is one of the major candidate materials for its high strength and thermal stability. In this study, in order to establish the data base of the 2D-C/C composite, the fracture data was obtained by simulating the crack expected to be generated under the VHTR condition and the oxidation effect on the fracture behavior was evaluated. Moreover, the fracture mechanism of the C/C composite was investigated through scanning electron microscope observation. This study showed that the oxidized matrix caused reduction of the fracture toughness and the reduction ratio was dependent on the density of matrix and a number cracks. With increasing the oxidation, the fracture toughness is mainly dependent on the fiber characteristics. Furthermore, the crack grows along the boundary between fiber bundles without breaking the fiber. The cracks which were initiated at the ...
Print ISSN:
1757-8981
Electronic ISSN:
1757-899X
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics