    Corrosion Embrittlement of Duralumin V : Results of Weather-Exposure Tests (1929)
    In:  CASI
    Details
    Publication Date: 2019-06-28
    Description: In a series of weather exposure tests of sheet duralumin, upon which accelerated corrosion tests in the laboratory by the wet-and-dry corrosion method in a sodium chloride solution has already been carried out, a close parallelism between the results of the two kinds of tests was found to exist. The exposure tests showed that the lack of permanence of sheet duralumin is largely, if not entirely, due to corrosion. A corrosion attack of an intercrystalline nature is very largely responsible for the degree of embrittlement produced. The rate of embrittlement was greatly accelerated by a marine atmosphere and by the tropical climate. Variations in corrosion and embrittlement are noted in relation to heat treatment, cold working, and types of protective coatings.
    Type: NACA-TN-304
    Format: application/pdf
    Location Call Number Expected Availability
    BibTip Others were also interested in ...
    NASA TECHNICAL REPORTS
Close ⊗
This website uses cookies and the analysis tool Matomo. More information can be found here...