Publication Date:
2019-06-28
Description:
Sodium-sulfate-induced hot corrosion of preoxidized IN-738 was studied at 975 C with special emphasis placed on the processes occurring during the long induction period. Thermogravimetric tests were run for predetermined periods of time, and then one set of specimens was washed with water. Chemical analysis of the wash solutions yielded information about water soluble metal salts and residual sulfate. A second set of samples was cross sectioned dry and polished in a nonaqueous medium. Element distributions within the oxide scale were obtained from electron microprobe X-ray micrographs. Evolution of SO was monitored throughout the thermogravimetric tests. Kinetic rate studies were performed for several pertinent processes; appropriate rate constants were obtained from the following chemical reactions: Cr2O3 + 2 Na2SO4(1) + 3/2 O2 yields 2 Na2CrO4(1) + 2 SO3(g)n TiO2 + Na2SO4(1) yields Na2O(TiO2)n + SO3(g)n TiO2 + Na2CrO4(1) yields Na2O(TiO2)n + CrO3(g).
Keywords:
METALLIC MATERIALS
Type:
NASA-TP-2319
,
E-1847
,
NAS 1.60:2319
Format:
application/pdf