Publikationsdatum:
2019-06-28
Beschreibung:
The primary mode of moisture ingress into bonded composite joints is determined using a nuclear probe for deuterium (NPD) to measure the localized D2O content along the length of the adhesive (FM-300 and EA-9601) and through the thickness of bonded composite speciments. Calculated diffusivities and NPD measured equilibrium moisture contents are used to predict the moisture profiles along the length of the adhesives as a function of exposure time, temperature, and relative humidity. These results are compared with the observed moisture profiles to evaluate the extent of enhanced edge diffusion. The FM-300 adhesive exhibits good agreement between measured and predicted profiles at 49 C, 70% and 90% RH, and 77 C, 70% RH. At 77 C, 90% RH, the measured moisture content near the adhesive edge is substantially larger than the predicted level. The EA-9601 adhesive also shows good agreement at 49 C, 70% and 90% RH, but at 77 C, the concentration of D20 near the edges is enhanced at each humidity level. The effect of moisture content on the bond shear strength at room temperature and at elevated temperature is evaluated.
Schlagwort(e):
COMPOSITE MATERIALS
Materialart:
NASA-CR-3387
,
RE-610
Format:
application/pdf