Publication Date:
2019-06-27
Description:
The propagation of ultrasonic pulses in pyrophyllite specimens was studied to determine the effect of specimen precompression on the measured elastic moduli. Measurements were made at room pressure and, for the precompressed specimens, to pressures of 3 kbar. Pyrophyllite was found to be elastically anisotropic, apparently the result of the fabric present in our material. The room pressure adiabatic bulk modulus as measured on specimens made of isostatically compacted powered pyrophyllite was determined to be 96.1 kbar. The wave speeds of ultrasonic pulses in pyrophyllite were found to decrease with increasing specimen precompression. A limiting value of precompression was found, above which no further decrease in wave speed was observed. For the shear wave speeds this occurs at 10 kbar while for the longitudinal wave at 25 kbar. In the limit, the shear waves propagate 20% slower than in the unprecompressed samples; for the longitudinal wave the difference is 30%.
Keywords:
STRUCTURAL MECHANICS
Type:
NASA-CR-142598
,
REPT-2366
Format:
application/pdf