Publication Date:
2019-06-27
Description:
Load capacities were determined for plain spherical bearings with self-lubricating spherical elements of graphite-fiber-reinforced-polyimide, and for plain cylindrical bearings with thin-wall liners of the composite in the bearing bores. Composites consisted of a 1-to-1 weight ratio of graphite fibers and polyimide. Oscillation was at an amplitude of + or - 15 deg at a frequency of 1 hertz. Bearings with composite ball material had a load capacity of approximately 69 MN/sq m (10 000 psi) at room temperature 25 MN/sq m (3600 psi) at 340 C (650 F). Bearings with thin-wall composite liners had much higher load capacities of 280 MN/sq m (40 000 psi) at room temperature amd 240 MN/sq m (35 000 psi) at 320 C (600 F). Friction coefficients were in the range of 0.12 to 0.19. The addition of 10 wt.% graphite fluoride solid lubricant to the composition of the thin-wall liners reduced friction coefficients into the range of 0.10 to 0.12.
Keywords:
MECHANICAL ENGINEERING
Type:
NASA-TN-D-7880
,
E-8118
Format:
application/pdf