Scientific.Net: Materials Science & Technology / Trans Tech Publications Archiv 1984-2008
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Notes:
Thin Mn2(NO3)2/PVA precursor nanowire was fabricated via electrospinning technology at alow temperature in this paper. After dried at 150°C for 10 hours and then sintered at 450°C for 2 hours,Mn2O3 nanowire was successfully obtained. The nanowire was characterized using X-ray diffraction andscanning electron microscopy. The results showed that the nanowire was composed of pure Mn2O3 phase.The nanowire exhibited smooth surface and continuous sharp with length of tens of micrometer. Thediameter of Mn2O3 nanowire was measured and calculated through SEM, which showed most probablevalue of about 110 nm and 270 nm. The reason of the diameter separation was also discussed
Type of Medium:
Electronic Resource
URL:
http://www.tib-hannover.de/fulltexts/2011/0528/01/56/transtech_doi~10.4028%252Fwww.scientific.net%252FKEM.368-372.532.pdf