Addition reaction of (3-methyl-3-oxetanyl)methyl acetate (MOMA) with bis(4-mercaptophenyl) sulfide (BMPS) was examined in certain organic solvents. When the reaction of MOMA with BMPS was performed without any catalyst in hexamethylphosphoric triamide (HMPA) and N-methyl-2-pyrrolidone (NMP) at 130°C for 24 h, conversions of the corresponding adduct were 96 and 36%, respectively, which was confirmed by 1H-NMR spectra. On the other hand, when the reaction was carried out using tetraphenylphosphonium bromide (TPPB) as a catalyst under the same conditions, conversions of the adduct were 96 and 81% in HMPA and NMP, respectively. This result shows that although the addition reaction of oxetane compound with aromatic dithiol proceeds without any catalyst in HMPA, the reaction was strongly enhanced by adding TPPB in NMP. On the basis of the above results, polyadditions of bis((3-methyl-3-oxetanyl)methyl) terephthalate (BMOT) and bis((3-ethyl-3-oxetanyl)methyl) terephthalate with BMPS were performed using TPPB as the catalyst in NMP at 130°C for 24 h. As a result, the corresponding high molecular weight polymers 1 (Mn = 22,400) and 2 (Mn = 12,800) with pendant primary hydroxyl groups were obtained in 83 and 89% yields without any gel products, respectively. Furthermore, a low molecular weight oligomer was obtained from the polyaddition of BMOT with aliphatic dithiol, bis(mercaptomethyl)benzene, under the same reaction conditions. The catalytic activity on the polyaddition of BMOT with BMPS was also examined, and it was found that thermally stable TPPB and crown ether complexes at the reaction temperature (130°C) have higher catalytic activity than tetrabutylammonium bromide and tetrabutylphosphonium bromide to produce polymer 1 with high molecular weight. © 1998 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 36: 2873-2880, 1998
Zusätzliches Material:
1 Ill.
Materialart:
Digitale Medien