A specimen of linear polyethylene was subjected to isothermal secondary crystallization at a series of temperatures below the primary isothermal crystallization temperature, the melting and primary crystallization stages being held constant throughout the investigation. Dilatometric measurements exhibit an S-character at low values of undercooling Tp - Ts, where Tp and Ts are, respectively, the primary and secondary crystallization temperatures, whereas at larger undercooling, an initial very rapid crystallization is followed by a very slow stage. When corrected for thermal contraction of the polymer, the net degree of secondary transformation is seen to peak at a temperature about 5°C below Tp. The S-character of the isotherms and the peaked temperature variation of degree of transformation lead to the conclusion that a large portion of the secondary crystallization consists of the nucleation and growth of the new crystallites. Johnson-Mehl-Avrami analysis leads to a model of heterogeneous nucleation within the remaining amorphous zones, followed by one-dimensional, diffusion-controlled growth.
Additional Material:
3 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/pol.1969.160070507