ISSN:
0044-2313
Keywords:
Protonated sodium layer silicate hydrate
;
29Si-, 23Na- and 1H-MAS-NMR
;
dehydration
;
Chemistry
;
Inorganic Chemistry
Source:
Wiley InterScience Backfile Collection 1832-2000
Topics:
Chemistry and Pharmacology
Description / Table of Contents:
On the Chemistry of Kanemite [NaHSi2O5 · 3 H2O]xStarting from δ-Na2Si2O5 Kanemit was prepared by a direct exchange of Na+ by H+ in water containing reaction mixtures. By 29Si-, 23Na- and 1H-MAS-NMR investigations Kanemit was characterized as a layersilicate [NaHSi2O5 · 3 H2O]. By thermal treatment as well as by dehydration at room temperature under vacuum conditions a monohydrate is formed in which the layerstructure remains nearly unchanged. At temperatures between 100 and 110°C under normal conditions a hydrate phase of the composition [NaHSi2O5 · 0.25 H2O]x is prepared in which a changed silicate-layerstructure exists.
Notes:
Kanemit wurde aus δ-Na2Si2O5 durch einen direkten Austausch von Na+ gegen H+ in wasserhaltigem Reaktionsmedium hergestellt. Mit Hilfe von 29Si-, 23Na- und 1H-MAS-NMR-Untersuchungen wurde nachgewiesen, daß der Kanemit ein Schichtsilicat der Zusammensetzung [NaHSi2O5 · 3 H2O]x ist. Bei der thermischen, wie auch bei der Entwässerung im Vakuum bei Raumtemperatur entsteht ein Monohydrat, in dem die Schichtstruktur weitgehend erhalten bleibt. Bei Temperaturen zwischen 100 und 110°C läßt sich auch eine Hydratphase der Zusammensetzung [NaHSi2O5 · 0,25 H2O]x nachweisen, in der aber eine veränderte Schichtsilicatstruktur vorliegt.
Additional Material:
8 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19956211029