Studies on Oxide Catalysts. XXXIV. Redoxbehaviour of Nickel in Zeolite NiNaY. 1. Reducibility and Reoxidizability of Nickel in Zeolites NiNaYThe properties of metallic nickel in reduced (470-870 K) and reoxidized (470, 670 K) samples were studied by chemical analysis (reaction with K2Cr2O7) and spectroscopic methods (FMR, IR after CO adsorption, UV/VIS). The reduction of Ni2+ cations from oxidic clusters proceeds in an onestep reaction. Contrary to this, isolated Ni2+ cations are reduced stepwise to Ni+ cations and subsequently to metallic nickel. The reduction degree depends in characteristic manner on the reduction temperature. Metallic nickel which was reduced at temperatures 〈 620 K, can be completely reoxidized at 470 K. Higher temperatures result in metallic aggregations which are not completely reoxidized even at 670 K.
Notes:
Die Eigenschaften von metallischem Nickel in reduzierten (470-870 K) und reoxydierten (470, 670 K) NiNaY-Proben wurden durch chemische Analyse (Reaktion mit K2Cr2O7) und spektroskopische Untersuchungen (FMR, IR nach CO-Chemisorption und UV/VIS) charakterisiert. Die Reduktion der Ni2+-Kationen oxidischer Cluster erfolgt einstufig, während isoliert lokalisierte Ni2+-Kationen über Ni+-Kationen zum Metall reduziert werden. Entsprechend der Lokalisierung und dem Austauschgrad ändert sich der Reduktionsgrad des Nickels in charakteristischer Weise mit der Reduktionstemperatur. Metallisches Nickel, das bei Temperaturen 〈 620 K erhalten wurde, kann bei 470 K vollständig reoxydiert werden. Höhere Reduktionstemperaturen führen zu Nickelaggregationen, die selbst bei 670 K nicht vollständig reoxydierbar sind.
Additional Material:
5 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19834990424