Description / Table of Contents:
The new ternary compound Mn2AlB2 was prepared from Mn, Al and B, crystallizing in the form of needles with metallic lustre from an excess of molten Al. The unit-cell of the compound is orthorhombic with a = 2.92, b = 11.08 and c = 2.89 Å (Space-group C 222; Z = 2). The boron atoms are arranged in chains, which are connected by the Al-atoms giving layers in (0 0 1). Each boron is surrounded by 6 Mn at the corners of a trigonal prisma. - Together with Mn3AlB2, single crystals of AlB2 were obtained with a partly substitution of Mn for Al atoms. The compositions of such mixed-crystals have been found to be Al0.75Mn0.25B2.
Notes:
Aus Mn, Al und B wurde eine ternäre Phase der Zusammensetzung Mn2AlB2 erhalten. Diese kristallisiert aus geschmolzenem Überschüssigem Aluminium in silberglänzenden Nadeln, zusammen mit den schon bekannten Verbindungen AlB2 und Al6Mn. Mn2AlB2 hat eine rhombisch-basisflächenzentrierte Elementarzelle mit den Achsen a = 2,92, b = 11,08 und c = 2,89 Å, in der 2 Formeleinheiten untergebracht sind. Die Raumgruppe ist C 222. Die Atom-Lagen wurden durch röntgenographische Einkristalluntersuchung ermittelt. Die Boratome sind in der (0 0 1)-Fläche in Ketten angeordnet, die durch die in der gleichen Fläche liegenden Aluminiumatome zu Schichten verknüpft werden. Die Manganatome ordnen sich in der Form trigonaler Prismen um die Boratome an. - Neben dem Mn2AlB2 wurden bei einigen Versuchen Einkristalle des AlB2 erhalten, die nach den Ergebnissen der Analyse entsprechend der Formel Al0,75Mn0,25B2 Mn-Atome auf Al-Plätzen des Gitters substituiert enthielten.
Additional Material:
3 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19663440304