The influence of water and dissolved gases on the corrosion behaviour of iron in liquid ammoniaOxygen increases the corrosion rate of active iron in liquid ammonia at + 20°C and passivates iron at concentrations exceeding a critical concentration which increases with the acidity. Water acts as an acid and increases the corrosion rate of passive iron up to 0.1 wt. %. At higher concentrations of water, corrosion is inhibited probably because of the precipitation of hydrated iron (III) oxide. Carbon dioxide always enhances the corrosion rate of passive iron acting as a strong acid and a strong complexing agent for iron (III). At high concentrations of carbon dioxide or ammonium carbaminate iron cannot be passivated.
Notes:
Sauerstoff erhöht die Korrosionsgeschwindigkeit des aktiven Eisens in flüssigem Ammoniak bei + 20 °C und passiviert das Eisen, sobald eine mit der Säurekonzentration abnehmende kritische Konzentration überschritten wird. Wasser wirkt als Säure und erhöht bis zu 0,1 Gew. % die Korrosionsgeschwindigkeit des passiven Eisens. Bei höheren Wassergehalten ist Wasser wahrscheinlich wegen der Ausfällung von hydratisiertem Eisen (III)-oxid ein Inhibitor. Kohlendioxid vergrößert stets die Korrosionsgeschwindigkeit des passiven Eisens. Es ist eine starke Säure und ein starker Komplexbildner für Eisen (III). Bei hohen Konzentrationen von Kohlendioxid oder Ammoniumcarbaminat kann das Eisen nicht mehr passiviert werden.
Additional Material:
8 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19810320502