Description / Table of Contents:
Corrosion inhibitors 25(1) - The role of the cation in a neutral salt in the corrosion of iron in the presence of oxygenThe rate of uptake of oxygen, under standard conditions, in the corrosion of 500 mg DAB6 iron powder is dependent on the nature of the cation in a neutral salt (chloride). In the presence of alkali, quaternary ammonium, quaternary phosphonium and alkali-earth chlorides, the rate of oxygen uptake is comparable. With zinc, cadmium, nickel and cobalt chlorides a marked decrease in the oxygen uptake is observed between pH5 and pH7. This is probably due to a block in the cathodic area in the iron boundary layer through precipitation of the rather insoluble basic hydroxides of zinc, cadmium, nickel and cobalt.
Notes:
Die Geschwindigkeit des Sauerstoffverbrauchs bei der Korrosion von jeweils 500 mg DAB6-Eisenpulver wird in Abhängigkeit von der Art des Kations in Neutralsalzen (Chloriden) unter Standardbedingungen bestimmt. In Gegenwart von Alkali-, Quartären Ammonium, Quartären Phosphonium-und Erdalkalichloriden ist die Geschwindigkeit des Sauerstoffverbrauches vergleichbar groß. Mit Zink-, Cadmium-, Nickel-und Kobaltchloriden wird aber im Bereich von pH5 bis pH7 eine überraschend große Verzögerung der Sauerstoffaufnahme beobachtet. Es handelt sich mit hoher Wahrscheinlichkeit um eine Blockade der kathodischen Bezirke in der Eisengrenzfläche durch Abscheidung der schwerlöslichen basischen Hydroxyde von Zink, Cadmium, Nickel und Kobalt.
Additional Material:
7 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19790300602