Influence of programmed welding temperature cycles on the resulting structure and the corrosion behavior of austenitic steelStudies on corrosion resistant austenitic steels subjected to simulated welding temperature cycles have shown that even after very short annealing times the corrosion resistance is decreased. In the temperature range between 700 and 900 °C carbides are precipitated, while grain growth and twinning are observed at temperatures between 900 and 1100 °C. Above 1280 °C delta-ferrite is formed as early as after 15 sec. Potentiokinetic current density/potential curves have been traced on the basis of tests in 1 N sulfuric acid at room temperature. The passivation current density has turned out to be a suitable corrosion resistance criterion.
Notes:
Untersuchungen an korrosionsbeständigen austenitischen Stählen, die simulierten Schweißtemperaturzyklen unterworfen wurden, zeigten, daß schon bei sehr kurzen Anlaßzeiten eine Verschlechterung der Korrosionsbeständigkeit auftrat. Im Temperaturgebiet von 700-900 °C kommt es zu Ausscheidungen von karbiden, während bei Temperaturen von 900-1100 °C Kornwachstum und Zwillingsbildung beobachtet wurde. Oberhalb 1280 °C bildet sich bereits nach 15 sec Deltaferrit. Es wurden poteniokinetische Stromdichte Potentialkurven in l - n Schwefelsäure bei Raumtemperatur aufgenommen. Als Maß zur Beurteilung der Korrosionsbeständigkeit erwies sich die Passivstrom dichte als geeignet.
Additional Material:
13 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19730240105