Surface potential profiles of metalsUsing a microcapillary method in connection with simultaneous metallographic observation surface potential profiles have been determined with the potential probe in alcoholic acid solutions on cast iron, CrNi aciers steels 188, Cr steel with 17% Cr (welded) and an AlCu alloy. It was possible to distinguish cementite from ledeburite, not however, from austenite. The potential of 188 steel under pitting conditions decreases as a linear function of pit depth. The appearance of potential minima in a weld of ferrite steels is evidence of a intercrystalline corrosion in that particular medium. The precipitation of CuAl2 in AlCu alloys at 150 °C at the grain boundaries forms an element with the grain boundary as the anode giving rise to intercrystalline corrosion.
Notes:
Mit Hilfe einer Mikrokapillarmethode in Verbindung mit gleichzeitiger metallographischer Beobachtung wurden mit einer Potentialsonde in alkoholischen Säuren die Oberflächenpotentiale von Roheisen, CrNi-Stahl 188, 17% Cr-Stahl (Schweißnaht) und einer AlCu—Legierung bestimmt. Dabei konnte Zementit von Ledeburit, nicht hingegen von Austenit unterschieden werden. Beim Lochfraß von 188 Stahl nimmt das Potential linear mit der Lochtiefe ab. Das Auftreten von Potentialminima in der Schweißnaht ferritischer Stähle ist ein Indiz für das Auftreten von interkristalliner Korrosion in dem betreffenden Medium. In AlCu—Legierungen wirken die bei etwa 150 °C entstehenden Ausscheidungen von CuAl2 an den Korngrenzen als Anode und führen dadurch zu interkristalliner korrosion.
Additional Material:
15 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19720230707