Description / Table of Contents:
Crack and fracture formation in austenitic CrNi steels in the specific conditions of stress corrosion cracking and corrosion fatigueEven in media producing stress corrosion craking the fatigue component dominates at frequencies around 50 Hz and is noticable at frequencies as low as 30 Hz. A typical feature of such failures is the appearance of intercrystalline fracture regions in the range of low crack propagation velocities. With decreasing tolerable load the fatigue component effect gradually disappears and crack formation is initiated by localized attack from the surrounding medium.
Notes:
Auch in Medien, welche Spannungsriß-korrosion hervorrufen, dominiert die Schwingungsrißkorrosionskomponente bei Frequenzen um 50 Hz; sie ist auch noch bei Schwingungen um 30 Hz merklich. Ein Charakteristikum derartiger Schäden ist das Auftreten interkristalliner Bruchbereiche im Gebiete niedriger Rißausbreitungsgeschwindigkeiten. Mit abnehmender ertragener Belastung ver schwindet die Ermüdungskomponente allmählich, und die Rißbildung wird durch vom umgebenden Medium ausgebenden örtlichen Angriff ausgelöst.
Additional Material:
11 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19720230506