Description / Table of Contents:
Oxidation of iron at high temperatures in inert gases with small oxygen contentsAt temperatures 〉 about 800°C and linear flow velocities of the gas between about 5 and 12 cm/s the oxidation of iron in N2-O2, Ar-O2 and He-O2 mixtures containing 〈 1% oxygen follows a linear kinetic law. Under such conditions the rate controlling step is the transport of oxygen from the gas phase to the surface of the scale layer which consists exclusively of FeO. The constant of the linear kinetic law under laminar flow conditions is proportional to the oxygen content of the gas and to the square root of the gas flow velocity, and inversely proportional to the square root of the gas viscosity, while it is practically independent from temperature. Some conclusions with reference to practical applications are presented.
Notes:
Eisen oxydiert bei Temperaturen 〉 etwa 800°C und bei linearen Strömungsgeschwindigkeiten des Gases zwischen etwa 5 und 12 cm/sec in N2-O2-, Ar-O2- und He-O2-Gemischen mit Sauerstoffgehalten 〈 1% nach einem linearen Zeitgesetz. Geschwindigkeitsbestimmend ist unter diesen Bedingungen der Antransport des Sauerstoffs aus der Gasphase an die Oberfläche der nur aus FeO bestehenden Zunderschicht. Die Konstante des linearen Zeitgesetzes ist bei laminarer Strömung proportional dem Sauerstoffgehalt des Gases, proportional der Quadratwurzel aus der Strömungsgeschwindigkeit des Gaseskehrt, umgekehrt proportional der Quadratwurzel aus der Viskosität des Gases und praktisch unabhängig von der Temperatur. Einige Schlußfolgerungen für die Praxis werden diskutiert.
Additional Material:
5 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19720230203