Description / Table of Contents:
Corrosion and mechanical stresses as a source of failure at the waterside of high pressure steam generatorsThe feasibility of using ferritic steels in contact with hot water in boiler and apparatus construction is due to the formation of a coherent magnetite layer which prevents damage by local corrosion even during short shouldown periods with admission of could aerated water. This protection may be lost when mechanical stresses result in a fracture of the protective layer. The interaction of mechanical stresses, deformations, thermal influences, cracking of the protective layer and shouldown corrosion can have a negative bearing on the safety of a construction or may result in serious failures.
Notes:
Die Einsatzmöglichkeit ferritischer Stähle im Dampfkessel- und Apparatebau beruht bei Berührung mit heißem Wasser und Dampf auf der Bildung einer geschlossenen Magnetitschicht, die auch bei kurzzeitigen Stillständen unter Zutritt von kaltem sauerstoffhaltigem Wasser eine Schädigung durch lokale Korrosion verhindert. Diese Schutzwirkung kann unter Mitwirkung mechanischer Spannungen durch Schädigung der Schutzschicht verlorengehen. Die Wechselwirkung von mechanischen Spannungen and Verformungen, thermischen Einflüssen, Schutzschichtschäden und Stillstandskorrosion kann zu einer Beeinträchtigung der Sicherheit einer Konstruktion oder sogar zu größeren Schadensfällen führen.
Additional Material:
14 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19710220409