The chemical equilibria encountered with the chromium-plating of steelIn order to determine the equilibrium conditions, the authors investigated, in the compound system Fe(s) + CrJ2(g) ⇌ Cr(s) + FeJ2(g) used for diffusion-type chromium plating, the two stages Cr(s)+ 2J(g) ⇌ CrJ2(g) and Fe(s) + 2J(g) ⇌ FeJ2(g) which determine the reaction rate. The former stage was investigated at a temperature range of 700 to 1160° C, the latter at 760 to 1080° C. In this temperature range, the equilibrium is shifted somewhat to the left, the shift increasing with higher temperatures. However, as the general correlation of the equilibrium constants with temperature is low, it may be assumed that chromium-plating could be carried out over a much wider temperature range than is usual at present.
Notes:
Für die Ermittlung der Gleichgewichts-beziehungen wurden in dem für die Diffusionsverchromung verwendeten Verbindungs-system Fe(f) + CrJ2(g) ⇌ Cr(f) + FeJ(g) die beiden geschwindigkeitsbestim-menden Schritte Cr(f)+ 2 J(g) ⇌ CrJ2,(g) und Fe(f) + 2 J(g) ⇌ FeJ2(g) untersucht, und zwar die erste bei 700-1100, die zweite bei 760 und 1080° C. Das Gleichgewicht ist im untersuchten Temperaturbereich etwas nach links verschoben, und zwar um so stärker, je höher die Temperatur ist. Die insgesamt geringe Temperaturabhängigkeit der Gleichgewichtskonstanten läßt jedoch vermuten, daß die Inchromierung in einem weit breiteren Temperaturbereich geführt werden kann als es bisher in der Praxis geschieht.
Additional Material:
2 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19690200208