Description / Table of Contents:
The application of radiotracer technique for the determination of small corrosion rates of tantalum, a tantalum-niobium-alloy and zirconium in azeotropic nitric acidThe radiotracer technique following neutron activation is a suitable means to measure hitherto hardly detectable, very low corrosion rates. In azeotropic nitric acid, tantalum and the tantalum-40niobium alloy show at 20 to 120°C approximately the same corrosion rates between 0.2 · 10-6 and 8 · 10-6 mm/a; the apparent activation energies are 30 to 40 kJ/mol.In the temperature region from 20 up to 81°C the corrosion rates of zirconium are between 7 · 10-6 and 5 · 10-4 mm/a; the apparent activation energy is 47 kJ/mol.In the case of zirconium, check measurements (analysis of the corrosive medium with AAS and ICP) with non-activated sheet-metal sections resulted in similar corrosion rates.
Notes:
Die Radiotracer-Methode nach Neutronenaktivierung ist geeignet, bisher kaum erfaßbare, sehr geringe Abtragungsraten zu bestimmen. Tantal und die Tantal-40Niob-Lergierung zeigen in azeotroper Salpetersäure bei 22 bis 120°C annähernd gleiche Abtragungsraten von 0,2 · 10-6 bis 8 · 10-6 mm/a; die scheinbaren Aktivierungsenergien betragen 30 bis 40 kJ/mol.Die Abtragungsraten von Zirconium liegen im Temperaturbereich von 20 bis 81°C zwischen 7 · 10-6 und 5 · 10-4 mm/a; die scheinbare Aktivierungsenergie ergibt sich zu 47 kJ/mol.Im Falle des Zirconiums führten Kontrollmessungen (Analyse des Angriffsmittels mit AAS und ICP) an nicht aktivierten Blechabschnitten zu vergleichbaren Abtragungsraten.
Additional Material:
5 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19900411003
Permalink