Description:
Sensitivity of the elevated temperature (above 0.5 Tm) deformation of TD-nickel to grain size and shape was examined in both tension and creep. Elevated temperature strength increased with increasing grain diameter and increasing L/D ratio. Temperature sensitivity of the yield stress, as well as high (compared to self diffusion) apparent tensile activation enthalpies were the result of the internal stress not being proportional to the shear modulus. Creep activation enthalpies increased with increasing L/D ratio and, to a lesser extent, increasing grain diameter, reaching high values which may be apparent values. The thoria particle dispersion may have been altered by elevated temperature tensile and creep deformation.