The characteristics of deformation of an orthorhombic phase based alloy, Ti-22Al-25Nb (at%), have been studied by hot compression tests in the temperature range of 940-1150℃ with the strain rates of 0.01s-1 and 0.1s-1. A flow curves typically controlled by dynamic recovery were observed in the temperature range of 1090-1150 ℃ for the strain rate of 0.01s-1 , while discontinuous yield phenomena was found for the strain rate of 0.1s-1. The dynamic recovery can be identified by the microstructure characteristics of the deformation specimens. At 1060℃, thetemperature of beta transus, the flow curves and microstructure exhibited the same deformation charateristics as that above the beta transus. At the subtransus temperature, a long period of flow softening followed by the steady-state flow can be observed. During the hot deformation, the hard phases α2 and O elongated, subboundary produced followed by cusp formation in the elongated α2 and O phases, the equiaxed morphology phases occurred by B2 phase penetrating along the subboundaries. The softening mechanism was discussed
Type of Medium:
Electronic Resource
URL:
http://www.tib-hannover.de/fulltexts/2011/0528/02/09/transtech_doi~10.4028%252Fwww.scientific.net%252FMSF.475-479.825.pdf
Permalink