Investigations of the Ionic Transport Properties in Solid CaSTransference measurements clearly indicate in direct manner the predominant motion of divalent Ca2+ ions in CaS. The ac impedance was measured as a function of the sulfur partial pressure in the range from 10-1 to 10-8 atm from 900 to 1300 K in the frequency range from 10 Hz to 170 kHz. The conductivity is independent of the sulfur partial pressure below about 10-5 atm and increases with the 6th root of the sulfur partial pressure at higher pS2 (1100 - 1300 K). The conductivity σ of CaS is 3.9 · 10-6 ω-1 cm-1 at 1000 K. The activation enthalpy of σ T is 1.15 eV. The dependence of the conductivity from the sulfur partial pressure is explained in terms of a Schottky type defect model for CaS.
Notes:
Überführungsmessungen an CaS zeigen eindeutig und auf direkte Weise, daß zweiwertige Calciumionen die überwiegend beweglichen Ladungsträger darstellen. Die Impedanz wurde im Frequenzbereich 10 Hz - 170 kHz als Funktion des Schwefelpartialdrucks von 10-1 bis 10-8 atm über das Temperaturintervall 900 - 1300 K gemessen. Die Leitfähigkeit ist unabhängig vom Schwefelpartialdruck unterhalb etwa 10-5 atm und steigt mit der 6. Wurzel aus dem Schwefelpartialdruck bei höheren Drücken an (1100 - 1300 K). Die Leitfähigkeit σ von CaS beträgt bei 1000 K 3,9 · 10-6 ω-1 cm-1. Die Aktivierungsenthalpie von σ T ist 1,15 eV. Die Abhängigkeit der Leitfähigkeit vom Schwefelpartialdruck läßt sich durch die Annahme eines Schottky-Fehlordnungsmodells erklären.
Additional Material:
6 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19834970209
Permalink