Alloy 600
;
Grain boundary structure
;
Misorientation texture
;
Life and Medical Sciences
;
Cell & Developmental Biology
Source:
Wiley InterScience Backfile Collection 1832-2000
Topics:
Natural Sciences in General
Notes:
Selected area channeling patterns imaged on an SEM are digitized and displayed on the screen of a Macintosh computer, on which the user selects channeling bands that are measured to determine orientation. Grain boundary misorientations are found using the orientation information for pairs of grains adjacent at grain boundaries, and the boundaries are classified as low angle boundaries (LABs), coincident site lattice boundaries (CSLBs), or general boundaries (GHABs) based on the misorientation information. The technique was implemented to analyze the grain boundary character distributions (GBCDs) in Ni-16Cr-9Fe. The GBCDs of solution annealed material were similar to those expected in an aggregate of randomly oriented polycrystals. However, sequential thermomechanical treatments (5% tensile strain + 945°C:75 min + 2% tensile strain + 890°C:15 h + 3% tensile strain + 890°C:20 h or 9% compressive strain + 890°C:20 h + 9% compressive strain + 890°C:20 h + 3% compressive strain + 890°C:15 h) applied after the solution anneal lowered the proportions of GHABs in the GBCDs from 76-79% to 47-64%. The CSL-enhanced GBCDs of both the tensile-deformed samples and the compression-deformed sample appear to have evolved mainly through impingement of twin and twin-related boundaries during recrystallization; the CSL-enhanced GBCD of a compression-deformed sample appears to have been influenced by grain rotation processes to a greater degree than were the tensile-deformed samples. The CSL boundaries in the CSL-enhanced GBCDs were, in general, closer to the exact CSL misorientations than were those in the near-random GBCDs of the solution annealed material. An analysis of the distribution of misorientation axes did not indicate any correlation between grain misorientation texture and GBCD evolution.
Additional Material:
13 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/jemt.1060190309
Permalink