Contribution to the Effect of Segregation on the Corrosion Resistance of Austenitic Cr-Ni-Mo-SteelsInvestigations of segregated austenitic Cr-Ni-Mo-steels by means of the Huey-test showed that even a short annealing at 800°C can reduce the corrosion resistance. Especially for steels having a pronounced segregation this reduction of corrosion resistance can be such that it hinders the practical application of the material. This sensitivity to corrosion can be explained by the formation of intermetallic phases from ferrite which appears in small quantities within the segregated areas. It can be reduced by slightly altering the chemical composition towards a better austenite-stability and by remelting the steels to lower their segregated.
Notes:
Die Untersuchung von austenitischen Cr-Ni-Mo-Stählen mittels Huey-Test ergab, daß bei Vorhandensein von Seigerungen bereits durch kurzzeitige Glühungen bei 800°C die Korrosionsbeständigkeit in einem für die Anwendung dieser Stähle nicht mehr zulässigen Ausmaß beeinträchtigt werden kann. Die Ursache für diese Korrosionsanfälligkeit liegt offenbar in der Entstehung von intermetallischen Phasen aus dem in Seigerungsbereichen in kleinen Mengen auftretenden Ferrit. Eine Verminderung der Seigerungskorrosion ist durch geringfügige Veränderung der Durchschnittszusammensetzung in Richtung höherer Austenitstabilität sowie durch Anwendung von Umschmelzverfahren zur Erniedrigung des Seigerungsausmaßes möglich.
Additional Material:
12 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19760270202
Permalink