Description / Table of Contents:
Corrosion by weld slag of refractory chromium nickel steels in radiative heating tubesThe elevated sulfur concentration in the weld slags on refractory steels with nickel contents between 10 and 48% has given rise to considerable corrosion and the steels were destroyed by the low melting NiS eutectic. This corrosion is more severe in atmospheres resulting from incomplete combustion than in oxidizing atmospheres. Corrosions have been encountered in nonwelded material, too; in this case the formation of NiS can be attributed to the presence of CaO in the blast furnace gas; the incrustations then formed behaved like the welding slag and absorbed sulfur from the gas. It is recommended in such cases to weld not with wire electrodes but to use the TIG method.
Notes:
Die hohe Schwefelkonzentration in der Schweißschlacke führte zu starker Korrosion hitzebeständiger Stähle mit Nickelgehalten zwischen 10 und 48%; die Stähle wurden durch das NiS-Eutektikum (niedriger Schmelzpunkt) zerstört. Der Angriff ist in unvollständig verbrannten Atmosphären stärker als in oxidierenden. Auch im nichtgeschweißten Material trat Korrosion auf; in diesem Fall war die Bildung des NiS bedingt durch die Anwesenheit von CaO in dem zur Heizung verwendeten Gichtgas; die Staubablagerungen verhielten sich dann wie Schweißschlacke und nahmen Schwefel aus dem Gas auf. Es empfiehlt sich daher, in solchen Fällen nicht mit Elektrode und Zusatzdraht zu schweißen, sondern nach dem WIG-Verfahren zu arbeiten.
Additional Material:
8 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19750260109
Permalink