Materials science forum
Vol. 500-501 (Nov. 2005), p. 295-302
ISSN:
1662-9752
Quelle:
Scientific.Net: Materials Science & Technology / Trans Tech Publications Archiv 1984-2008
Thema:
Maschinenbau
Notizen:
In the production with thin slab casting a serious problem of insufficient grainrefinement and microstructural inhomogeneity has been found. In this paper attention has been paid to the austenite grain size changes in thin slab of a high strength Nb microalloyed steel under as-cast conditions and after first rolling pass. For comparison, the conventional thick slab was also investigated. It was found that although as-cast thin slab shows a smaller average austenite grain size than that of as cast thick slab; the latter after reheating shows a much finer average austenite grain size. The first rolling pass at high temperature and with heavy reduction causes rapid recrystallization that contributes to austenite grain refinement
Materialart:
Digitale Medien
URL:
http://www.tib-hannover.de/fulltexts/2011/0528/02/11/transtech_doi~10.4028%252Fwww.scientific.net%252FMSF.500-501.295.pdf
Permalink
|
Standort |
Signatur |
Erwartet |
Verfügbarkeit |