The cavitation erosion behavior of Fe-Cr-C-Si-xNi (x = 1, 2 and 3 wt.%) alloys were investigated for 50 hours using a 20 kHz vibratory cavitation erosion test equipment. 1 wt.% Ni added Fe-based hardfacing alloy showed excellent cavitation erosion resistance, comparable to the stellite 6. Above 1 wt.% Ni, however, the erosion resistance deteriorated quickly. It is conjectured that Ni addition above 1 wt.%, which has been shown to increase the stacking fault energy (SFE),resulted in reduction of the work hardening rate during the erosion test. Therefore, the enhanced cavitation erosion resistance of the 1 wt.% Ni alloy over the 2 and 3 wt.% Ni alloys could be explained in terms of the SFE, Ms temperature and work hardening
Type of Medium:
Electronic Resource
URL:
http://www.tib-hannover.de/fulltexts/2011/0528/02/12/transtech_doi~10.4028%252Fwww.scientific.net%252FMSF.510-511.274.pdf
Permalink