Lattice-matched GaN layers are grown by metalorganic chemical-vapor deposition on free-standing GaN substrates, which were fabricated by laser-induced liftoff of 300-μm-thick films grown by hydride vapor-phase epitaxy. Pretreatment of the free-standing films before the homoepitaxial growth of GaN involved mechanical polishing of the Ga-face surface and a final Cl-based plasma etch. By a combination of high-resolution x-ray diffraction, atomic-force microscopy, as well as Raman and photoluminescence spectroscopy, the structural and optical properties of the lattice-matched GaN layers are characterized. X-ray diffraction patterns of (0002), (0004), and (0006) reflexes with a full width at half maximum (FWHM) of as low as 20 arcsec are obtained. The dislocation density is determined to be 2×107 cm−2 and the surface morphology is dominated by bilayer steps with terraces of about 200 nm. The lattice mismatch between the GaN substrate and the homoepitaxial layer is below 3×10−5, resulting in a very narrow FWHM of the excitonic luminescence of 0.5 meV. © 2000 American Institute of Physics.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1063/1.1311596
Permalink