PETP samples were crystallized in different manner, and the resulting lamellar structures were investigated by X-ray diffraction, DSC, NMR, und Raman spectroscopy. In dependence on the crystallization conditions, lamellar thicknesses between 1.5nm and 2.5nm, rigid amorphous regions (interface) of about 2nm, and mobile amorphous regions with 1 nm to 3 nm were obtained. In the latter ones the rearrangement processes take place which are connected with the thermal glass transition. The thicknesses of these regions are related to the correlation length of the rearrangement processes determined via the glass transitions.
Notes:
Mit Röntgenbeugungs-, kalorimetrischen, NMR- und ramanspektroskopischen Untersuchungen werden Aussagen zur lamellaren Struktur von unterschiedlich kristallisierten PETP-Proben gemacht. Die verwendeten Kristallisations-regime ergeben Lamellendicken von 1,5 nm bis 2,5 nm, starre amorphe Bereiche (Randschichten) von etwa 2 nm und beweglich amorphe Bereiche von 1 nm bis 3 nm, in denen die mit dem thermischen Glasübergang verknüpften Umlagerungsprozesse ablaufen. Die Dicke dieser Bereiche entspricht den aus den Glasübergängen ermittelten Korrelationslängen der Umlagerungsprozesse.
Additional Material:
6 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/actp.1988.010391211
Permalink