Primary and tertiary amine-initiated polymerizations of L-alanine-N-carboxyanhydride (L-Ala-NCA) were conducted at 20 or 100°C in a variety of solvents. The 75.5-MHz 13C-nmr CP/MAS spectra of the resulting poly(L-alanines) revealed that all samples contain both α-helix and pleated-sheet structures. Depending on the reaction conditions the α-helix content varied between ca. 1 and 99%. Reprecipitation from aprotic nonsolvents does not change the α-helix/β-sheet ratio, indicating that this ratio is thermodynamically controlled. Since relatively large amounts of oligopeptides of degree of polymerization (DP) 4-6 can be extracted by means of acetic acid, it is concluded that (a) most poly(L-alanines) possess a bimodal molecular weight distribution, (b) the oligopeptide fraction with DP ≤ 11 is responsible for the β-sheet fraction of all samples, and (c) the two-stage crystal growth proposed by Komoto and Kawai is not correct. Solubilizing initiators such as poly(ethylene oxide) NH2 prevent the precipitation of oligoalanine and, thus, the formation of a β-sheet structure. 13C-nmr CP/MAS measurements also show that tri- and tetra-L-alanines form insoluble β-sheet structures.
Zusätzliches Material:
6 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/bip.360220508
Permalink