Irradiation sterilization is in wide use among tissue banks, for both hard and soft tissue grafts. Irradiation of tendon can impair its mechanical properties. Following implantation of a tendon graft, re-vascularization and resorption processes reduce its mechanical performance. Tendon with severely impaired properties may not be suitable for use as a load-bearing graft, e.g. as anterior cruciate ligament replacement. An important factor determining the extent of the reduction of the mechanical performance is the condition of the tendon during irradiation, especially the presence of water. There has not yet been a study of the effects of both irradiation dose and hydration on tendon mechanical properties. This study measured the changes in tensile mechanical properties, including strength and stiffness, following γ irradiation doses of 15 kGy (1.5 MRad) and 25 kGy (2.5 MRad), in the frozen state and following freeze-drying. The strength of the freeze-dried irradiated tendons was lower compared to fresh tendons, whereas the strength of the frozen irradiated tendons was very similar to that of the fresh. The tangent modulus of both of the freeze-dried irradiated groups were lower than the fresh tendons, as was the 15 kGy frozen group. The modulus of the 25 kGy frozen irradiated group was similar to the fresh. The general pattern of the results indicate that the two freeze-dried tendon groups were more affected than the frozen irradiated, and of the frozen irradiated groups the 25 kGy group was least affected. The results fit well with suggested mechanisms for the action of irradiation upon collagen; that intramolecular crosslinking and scission of the tropocollagen α chains occur when water is present, and α chain scission alone occurs when water is absent. lrradiation of tendons for use as grafts may produce minimal deleterious changes if the irradiation is performed while the tendon is frozen with water present.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF00123402
Permalink