Description / Table of Contents:
Investigations into sodium corrosion of austenitic materials at 1000 °CA series of austenitic materials with sufficiently high strength for the use at high temperatures were examined in respect to their compatibility with liquid sodium at 1000 °C. Austenitic steels with nickel contents of 12% showed the highest stability, but materials with 32% nickel and 20% chromium suffered also moderate losses of weight, however, additional internal corrosion effects. Nickelbase alloys were most severely attacked. They are less applicable for the use with sodium of very high temperatures in spite of their high temperature strengths.
Notes:
Eine Reihe austenitischer Werkstoffe, die für den Einsatz bei hohen Temperaturen hinreichende Festigkeit aufweisen, wurden auf ihre Beständigkeit gegen flüssiges Natrium bei 1000 °C untersucht. Die höchste Beständigkeit wiesen austenitische Stähle mit etwa 12% Nickel auf, aber auch die Werkstoffe mit 32% Nickel und 20% Chrom zeigten nur mäßige Gewichtsverluste, allerdings auch innere Korrosionseffekte. Nickelbasislegierungen wurden am stärksten angegriffen und sind trotz ihrer hohen Festigkeit für den Einsatz mit Natrium bei sehr hohen Temperaturen weniger geeignet.
Additional Material:
7 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19890400902
Permalink