The phase and orientation of manganese nitride grown on MgO(001) using molecular beam epitaxy are shown to be controllable by the manganese/nitrogen flux ratio as well as the substrate temperature. The most N-rich phase, θ phase (MnN), is obtained at very low Mn/N flux ratio. At increased Mn/N flux ratio, the next most N-rich phase, the η phase (Mn3N2), is obtained having its c axis normal to the surface plane. Further increasing the Mn/N flux ratio, the η phase (Mn3N2) having its c axis in the surface plane is obtained. Finally, the cursive-epsilon phase (Mn4N) is obtained at yet higher Mn/N flux ratio. The structural phase variation with Mn/N flux ratio is due to the kinetic control of the surface chemical composition, which determines the energetically most favorable phase. For a given Mn/N flux ratio, the phase is also found to be a function of the substrate temperature, with the less N-rich phase occurring at the higher substrate temperature. The change of phase with temperature is attributed to the change in the chemical composition resulting from the diffusion of N vacancies. Since the magnetic properties of MnxNy depend on the phase, the Mn/N flux ratio provides a way of directly controlling the magnetic properties. A phase diagram for molecular beam epitaxial growth is presented. © 2002 American Institute of Physics.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1063/1.1425435
Permalink