C f /SiC composites were fabricated using fiber coatings including CNTs and matrix infiltration using the polymer impregnation and pyrolysis process. Interface between fiber and CNTs (CF/CNTs) was tailored to optimize mechanical properties of hybrid composites. The tailored interphases, such as Pyrocarbon (PyC) and PyC/SiC, protect fibers from degradation during the growth of CNTs successfully. Hybrid composites with well-tailored CF/CNTs interface displayed significantly increased mechanical strength (352 ± 21 MPa) compared with that (34 ± 3 MPa) of composites reinforced with CNTs, which grown on carbon fibers directly. The interfacial bonding strength of hybrid composites was improved and optimized by tailoring the CF/CNTs interface. Interfacial failure modes were studied, and a firm interface bonding at the joint where CNTs grown was observed.
Print ISSN:
1546-542X
Electronic ISSN:
1744-7402
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Permalink