Publication Date:
2013-08-31
Description:
Thermomechanical analysis (TMA), differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA) were performed on samples of RTV 511 exposed on the Long Duration Exposure Facility (LDEF) mission for 6 years in orbit and unexposed RTV 511 control samples. Slices 20- to 400-microns thick were removed from the exposed surface down to a depth of 1,500 microns through the 3-mm thick samples. The TMA and DSC results, which arise from the entire slice and not just its surface, showed no significant differences between the LDEF exposed and the control samples. TMA scans were run from ambient to 500 C; results were compared by a tabulation of the onset temperatures for flow. DSC scans were run from ambient to 600 C; no endotherms or exotherms occurred over the range observed. What appear to be glass transition temperatures were compared for the samples as a function of section depth within the sample and between the exposed and control samples. The TGA scans from 25 to 900 C, which arise from the surface of the sample initially, showed a slight increase in the top most 105-micron slice (the exposed, discolored side) in the weight loss at 600 C in oxygen. This weight loss dropped to bulk values at the next slice below the top section, a mean depth of 258 microns. The control sample also showed an increase in weight loss as the top surface was approached, but the 600 C weight losses were very inconsistent. The LDEF RTV sample appears to be mechanically undamaged, with a surface layer which oxidizes slightly faster as a result of orbital exposure.
Keywords:
INORGANIC AND PHYSICAL CHEMISTRY
Type:
NASA. Marshall Space Flight Center, LDEF Materials Results for Spacecraft Applications; p 455-463
Format:
application/pdf
Permalink