ALBERT

Description: Three and four-sheet expanded titanium sandwich sheets have been developed at Douglas Aircraft Company, a division of McDonnell Douglas Corporation, under contract to NASA Langley Research Center. In these contracts, spot welding and roll seam welding are used to join the core sheets. These core sheets are expanded to the face sheets and diffusion bonded to form various type cells. The advantages of various cell shapes and the design parameters for optimizing the wing and fuselage concepts are discussed versus the complexity of the spot weld pattern. In addition, metal matrix composites of fibers in an aluminum matrix encapsulated in a titanium sheath are aluminum brazed successfully to the titanium sandwich face sheets. The strength and crack growth rate of the superplastic-formed/diffusion bonded (SPF/DB) titanium sandwich with and without the metal matrix composites are described.

Description: The superplastically formed diffusion-bonded (SPF/DB) program has developed successfully and far enough to recommend that a major structural program to validate the weight and cost of SPF/DB sandwich titanium structure should be initiated. The NASA Langley study of wing and fuselage SPF/DB sandwich panels shows that this process is potentially structurally efficient. The Douglas SPF/DB expanded sandwich process that utilizes a welded core sheet that expands to face sheets proves to be very efficient. The theoretical weight optimization design charts for the wing and fuselage concepts were validated by small-scale tests. Mnay design applications were fabricated. Projecting the results of an SPF/DB sandwich airframe structure to a MDC AST design shows significant weight and cost savings. A 6 percent lower direct operating cost was calculated. A growth AST utilizing composites, metal matrices, and SPF/DB sandwich shows future promise for a post-1990 technology readiness. Titanium SPF/DB sandwich, compared to presently available aluminum structure, is superior for application to a Mach 2.2 supersonic transport.

Description: The major efforts leading to an efficient structural design include: (1) the analysis methods used to improve the structural model optimization and compare the structural concepts, (2) the analysis and description of the fail-safe, crack growth, and residual strength studies and tests, (3) baseline structural trade studies to determine optimum structural weights including effects of geometry changes, strength, fail-safety, aeroelastics and flutter, 6AL-4V annealed titanium in structural efficiency after 70,000 hours at temperature, (5) the study of three structural models for aircraft at 2.0 Mach, 2.2 Mach, and 2.4 Mach cruise speeds, (6) the study of many structural concepts to determine their weight efficiencies; and (7) the determination of the requirements for large-scale structural development testing.

Description: For laminar flow to be achieved, any protuberances on the surface must be small enough to avoid transition to turbulent flow. However, the surface must have joints between the structural components to allow assembly or replacement of damaged parts, although large continuous surfaces can be utilized to minimize the number the number of joints. Aircraft structural joints usually have many countersunk bolts or rivets on the outer surface. To maintain no mismatch on outer surfaces, it is desirable to attach the components from the inner surface. It is also desirable for the panels to be interchangeable, without the need for shims at the joint, to avoid surface discontinuities that could cause turbulence. Fabricating components while pressing their outer surfaces against an accurate mold helps to ensure surface smoothness and continuity at joints. These items were considered in evaluating the advantages and disadvantages of the joint design concepts. After evaluating six design concepts, two of the leading candidates were fabricated and tested using many small test panels. One joint concept was also built and tested using large panels. The small and large test panel deflections for the leading candidate designs at load factors up to +1.5 g's were well within the step and waviness requirements for avoiding transition.The small panels were designed and tested for compression and tension at -65 F, at ambient conditions, and at 160 F. The small panel results for the three-rib and the sliding-joint concepts indicated that they were both acceptable. The three-rib concept, with tapered splice plates, was considered to be the most practical. A modified three-rib joint that combined the best attributes of previous candidates was designed, developed, and tested. This improved joint met all of the structural strength, surface smoothness, and waviness criteria for laminar flow control (LFC). The design eliminated all disadvantages of the initial three-rib concept except for unavoidable eccentricity, which was reduced and reacted satisfactorily by the rib supports. It should also result in a relatively simple low-cost installation, and makes it easy to replace any panels damaged in the field.

Description: Many structural concepts for a wing leading edge laminar flow control hybrid panel were analytically investigated. After many small, medium, and large tests, the selected design was verified. New analytic methods were developed to combine porous titanium sheet bonded to a substructure of fiberglass and carbon/epoxy cloth. At -65 and +160 F test conditions, the critical bond of the porous titanium to the composite failed at lower than anticipated test loads. New cure cycles, design improvements, and test improvements significantly improved the strength and reduced the deflections from thermal and lateral loadings. The wave tolerance limits for turbulence were not exceeded. Consideration of the beam column midbay deflections from the combinations of the axial and lateral loadings and thermal bowing at -65 F, room temperature, and +160 F were included. Many lap shear tests were performed at several cure cycles. Results indicate that sufficient verification was obtained to fabricate a demonstration vehicle.