Publication Date:
2013-08-31
Description:
Effect of Niobium substitution at the copper site in YBa2Cu3O(7-x) was studied in thin film form. The films were deposited by laser ablation technique using the targets of the YBa2Cu(3-x)Nb(x)O(y) where x = 0.0, 0.025, 0.05, 0.1, 0.2, 0.4, 0.8 and 1.0 under identical deposition conditions on SrTiO3 (100) substrates. Films were characterized by XRD, resistivity, I-V and J(sub c) measurements. Films made from x = 0.025 and 0.05 concentrations of Nb substituted targets showed relatively improved superconducting properties compared to that of undoped films. the best J(sub c) realized for x - 0.025 Nb concentration was 1.8 x 10(exp 6) A/sq cm and for 0.05 Nb concentration it was 3.2 x 10(exp 6) A/sq cm at 77 K. However, degradation of the superconducting properties, with the increase of x is greater than or equal to 0.1 Nb concentration and drastic suppression and complete loss of superconductivity was noticed for x is greater than or equal to 0.4. The growth of impurity phase YBa2NbO6 for x = 0.1 and above of Nb concentration was noted from XRD (X-Ray Diffraction) patterns. However, the site occupancy of Nb could not be confirmed from these studies.
Keywords:
SOLID-STATE PHYSICS
Type:
NASA. Johnson Space Center, Proceedings of the 4th International Conference and Exhibition: World Congress on Superconductivity, Volume 2; p 762-76
Format:
application/pdf
Permalink