The tensile properties of both cis- and trans-polyacetylene, (CH)x, were investigated in order to determine the variables that influence that ultimate extension ratio (l/l0) of polyacetylene films. It was found that when cis-films of polyacetylene were extended in an inert (argon) atmosphere, ultimate extension ratios as high as 3.3 were obtained and with subsequent isomerization at 160-200°C under stress, a final l/l0, of about 4 was obtained. The extension ratio is extremely sensitive to exposure to oxygen and decreases markedly after periods as short as 1 min. It appears as though crosslinking may occur in the polymer when it is exposed to air and this produces brittleness in the specimen. When (CH)x was isomerized from cis to trans, it became brittle, even in the absence of air.
Additional Material:
8 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/pol.1980.180180303
Permalink