Publication Date:
2015-08-08
Description:
In this paper, using a hot-rolled and recrystallized Zr-1Sn-0.3Nb alloy sheet, five strain levels (10, 20, 30, 45 and 60%) of uniaxial compression experiments were performed at 700 o C with a strain rate of 0.001s -1 using a Gleeble 1500D thermal simulator. The morphologies, distributions and misorientations of the grain boundaries at different strains were characterized by an electron backscatter diffraction (EBSD) technique. The EBSD maps indicated that dynamic recrystallization occurred during the high-temperature deformation. The processes, namely, grain boundary bulging, strain induced subboundaries around the bulged grain boundaries and their transformation from low misorientation to high misorientation, were considered as the formation mechanisms of recrystallized grains. At the early stage of deformation, low angle boundaries (LABs) formed in grains, the original grain boundaries become serrated, and LABs formed around the serrated boundaries. With incr...
Print ISSN:
1757-8981
Electronic ISSN:
1757-899X
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Permalink