Magnesium aluminum oxynitride (Mg0.27Al2.58O3.73N0.27, termed as MgAlON) ceramics with high transparency and complicated shape was prepared by aqueous gelcasting, pressureless sintering, and followed by hot isostatic pressing. No obvious hydration was found by the characterizations of X‐ray diffraction, pH value, Fourier transform infrared and thermal analysis for the interaction between MgAlON spinel powders and water, leading to the stable MgAlON slurry with high solid loading (52 vol%) and low viscosity. This result may be due to different composition of MgAlON from that of MgAl2O4 and AlON. Besides, transparent MgAlON ceramic (1.95 mm in thickness) with a high in‐line transmittance ~86.3% at 3.7 μm was fabricated. The refractive index ~1.7499 at 589.3 nm and absorption coefficient ~1.2 cm−1 at 5 μm of MgAlON are between those of AlON and MgAl2O4 transparent ceramics, and Abbé number ~73.66 of MgAlON is the highest.
Print ISSN:
0002-7820
Electronic ISSN:
1551-2916
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
,
Physics
Permalink