Abstract— Fatigue strength, crack initiation and small crack growth behaviour in two kinds of squeeze-cast aluminium alloys, AC8A-T6 and AC4C-T6 were investigated using smooth specimens subjected to rotatary-bending fatigue at room temperature. Fatigue resistance of these alloys was almost the same as that of the wrought aluminium alloys because of their fine microstructure and of the decrease in defect size due to squeeze-casting. Fatigue crack initiation sites were at the eutectic silicon particles on the surface of specimens or at internal microporosity in the specimens. Crack initiation life, defined as a crack length of 50 μm on the specimen surface, was successfully estimated from an evaluation of initiation sites using fracture mechanics and the statistics of extrema. Small fatigue crack growth in the two kinds of alloys obeys the relation proposed by Nisitani et al., namely that d(2c)/dN = C(σa/σB)n· (2c), where C is a constant and σB is the ultimate tensile strength. It is pointed out that an improvement in fatigue strength of cast aluminium alloys can be expected by refining the eutectic silicon rather than by an increase in static strength.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1111/j.1460-2695.1997.tb00281.x
Permalink