A set of isothermally melt-crystallized polyethylene samples was examined using small-angle x-ray scattering (SAXS). Time and temperature of crystallization were the variable parameters used to create the set of samples. Following background subtraction, desmearing, and application of the Lorentz factor to the raw SAXS data it is possible to see many orders of reflection. This suggests that much higher degrees of order are present in isothermally melt-crystallized samples than had previously been thought possible. A combination of SAXS and DSC data indicates that there is no evidence for isothermal thickening in these samples. This study, coupled with data obtained from PE single crystals, produced information concerning the extrapolation of single-crystal data to fit bulk systems. In addition, the equilibrium melting point T0m determined is somewhat lower than previously claimed. This study also suggests that the surface energy of the mature crystals is always lower than that of the nucleated state and/or the nucleation factor Kσen increases with decreasing supercooling.
Zusätzliches Material:
11 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/pol.1981.180191008
Permalink